Salt spray testing machine/equipment(GW-032)
Â
| Model | GW-032A | GW032B | GW-032C |
| Inside box size(cm) | 60x45x40 | 90x60x50 | 120x80x50 |
| Outside box size(cm) | 107x60x118 | 141x88x128 | 190x110x140 |
| Testing room temperature | Salt test (NSS ACSS)35±1  degree / Corrosion Test (CASS)50±1 degree | ||
| Pressure barrel temperature | Salt test (NSS ACSS)47±1 degree / Corrosion Test (CASS)63±1 degree | ||
| Brine temperature | 35±1 degree or 50±1 degree | ||
| Testing room Capacity | 108L | 270L | 480L |
| Brine tank capacity | 15L | 25L | 40L |
| Salt concentration | The concentration of sodium chloride 5% or the 5% concentration of sodium chloride add 0.26g per liter of copper chloride (CuCl2 2H2O) | ||
| Air pressure | 1.00±0.01kgf/cm2 | ||
| Spray volume | 1.0~2.0ml/80cm2/h (working at least 16 hours, and then take the average) | ||
| Testing room relative humidity | 85% above | ||
| PH | 6.5~7.2Â Â 3.0~3.2 | ||
| Spray form | Programmable spray (Including continuous and intermittent spray) | ||
| power | AC220V1Φ10A | AC220V1Φ15A | AC220V1Φ20A |
Brief introduction:
This tester is used to test the anti-erosion quality of the surface of all materials after the rustproof of painting, coating, electroplating, anoding and rustproof greasing.
Standard for:
1. GB/T 2423.17-1993 salt spray test
2. GB/T 2423.18-2000 salt spray test
3. GB/T 10125-1997 salt spray test
4. ASTM B117-97 salt spray test
5. JIS H8502 salt spray test
6. IEC68-2-11 salt spray test
7. IEC68-2-52 1996 salt spray test
8. GB 10587-89 salt spray test
9. CNS 4158 salt spray test
10. CNS 4159 CASS Accelerated acetic acid copper salt spray test
11. GB/T 12967.3-91 CASS Accelerated acetic acid copper salt spray test
ISO-9227, ASTM-B117, JIS-D0201, H8502, H8610, Z2371, GB/T10125
Attached accessories:
Two bottle of NaClÂ
one Pcs 2000ML  glass beaker
Salt spray testing machine/equipment(GW-032)
Â
| Model | GW-032A | GW032B | GW-032C |
| Inside box size(cm) | 60x45x40 | 90x60x50 | 120x80x50 |
| Outside box size(cm) | 107x60x118 | 141x88x128 | 190x110x140 |
| Testing room temperature | Salt test (NSS ACSS)35±1  degree / Corrosion Test (CASS)50±1 degree | ||
| Pressure barrel temperature | Salt test (NSS ACSS)47±1 degree / Corrosion Test (CASS)63±1 degree | ||
| Brine temperature | 35±1 degree or 50±1 degree | ||
| Testing room Capacity | 108L | 270L | 480L |
| Brine tank capacity | 15L | 25L | 40L |
| Salt concentration | The concentration of sodium chloride 5% or the 5% concentration of sodium chloride add 0.26g per liter of copper chloride (CuCl2 2H2O) | ||
| Air pressure | 1.00±0.01kgf/cm2 | ||
| Spray volume | 1.0~2.0ml/80cm2/h (working at least 16 hours, and then take the average) | ||
| Testing room relative humidity | 85% above | ||
| PH | 6.5~7.2Â Â 3.0~3.2 | ||
| Spray form | Programmable spray (Including continuous and intermittent spray) | ||
| power | AC220V1Φ10A | AC220V1Φ15A | AC220V1Φ20A |
Brief introduction:
This tester is used to test the anti-erosion quality of the surface of all materials after the rustproof of painting, coating, electroplating, anoding and rustproof greasing.
Standard for:
1. GB/T 2423.17-1993 salt spray test
2. GB/T 2423.18-2000 salt spray test
3. GB/T 10125-1997 salt spray test
4. ASTM B117-97 salt spray test
5. JIS H8502 salt spray test
6. IEC68-2-11 salt spray test
7. IEC68-2-52 1996 salt spray test
8. GB 10587-89 salt spray test
9. CNS 4158 salt spray test
10. CNS 4159 CASS Accelerated acetic acid copper salt spray test
11. GB/T 12967.3-91 CASS Accelerated acetic acid copper salt spray test
ISO-9227, ASTM-B117, JIS-D0201, H8502, H8610, Z2371, GB/T10125
Attached accessories:
Two bottle of NaClÂ
one Pcs 2000ML  glass beaker
Alumina ball is a high-quality grinding medium made of selected high grade material, advanced molding technology and calcined in high temperature tunnel kiln. Possessed with high density, high hardness, low wear, good seismic stability and good corrosion resistance, the products are the most ideal medium for grinding glaze, blank and mineral powder processing, and are used as the grinding medium of ball mill in ceramics, cement, paint, refractory, inorganic mineral powder and other industries.
|
Commodity |
Alumina ball 30mm |
|
Appearance |
Faint yellow |
|
Al2O3 Content (%) |
≥70%±2% |
|
Bulk Density |
3.02(g/cm3) |
|
Water absorption |
<0.01(%) |
|
Degree of hardness (MOhs) |
8 |
|
Use raw material |
Fining high bauxite |
|
Formation way |
Isostatic pressing |
Alumina Ball 30,92% Alumina Ball,High Quality Alumina Balls,High Alumina Grinding Bead Ceramic Balls
Shanxi Ruineng Ceramic Material Co.,Ltd , https://www.rnceramic.com